    Item type:Publication,
    Aging-induced enhancement of corrosion resistance in Al-4Ni-1Mn alloys through Al3(Sc, Zr) precipitates
    (2025-05-05)
    Masthong, Anuchit
    ;
    Eskin, Dmitry
    ;
    Limmaneevichitr, Chaowalit
    ;
    Pandee, Phromphong
    ;
    Diewwanit, Onnjira
    Al-Ni-Mn alloys are attractive for high-temperature, corrosive environment due to the formation of stable intermetallic compounds that can reduce corrosion susceptibility. This study showed that the additions of Mn, Sc, and Zr in Al-4 % Ni alloys significantly enhanced hardness and thermal stability through the simultaneous effect of transformation of the Al + Al<inf>3</inf>Ni to Al + Al<inf>9</inf>(Ni, Mn)<inf>2</inf> eutectic and precipitation of Al<inf>3</inf>(Sc, Zr). The thermal stability of an Al-4 % Ni-1 % Mn alloy was very good when exposed to 350 °C for 60 h. Additionally, the hardness substantially increased in an Al-4 % Ni-1 % Mn alloy with the addition of Sc and Zr, showing an approximate increase of 30 %. The highest hardness achieved was approximately 50 % higher with the optimal Sc and Zr content as compared to the Al-4Ni-1Mn alloy. Addition of 1 % Mn to an Al-4 % Ni alloy decreased the current density (I<inf>corr</inf>) and increased the corrosion potential (E<inf>corr</inf>), indicating better corrosion resistance. The effects of Sc and Zr additions on corrosion were also investigated, revealing that the increased Sc and Zr content led to more aggressive corrosion in the as-cast condition due to the eutectic coarsening and a high solid solution concentration of Sc and Zr that led to microstructural instability and electrochemical effects. However, after aging at 350 °C, the corrosion resistance significantly improved due to the Al<inf>3</inf>(Sc, Zr) precipitates that interrupted the corrosion path.
  • Loading...
    Thumbnail Image
    Some of the metrics are blocked by your 
    consent settings
    Item type:Publication,
    Characterization of the Anodic Film and Corrosion Resistance of an A535 Aluminum Alloy after Intermetallics Removal by Different Etching Time
    (2022-07-01)
    Chankitmunkong, Suwaree
    ;
    Eskin, Dmitry
    ;
    Limmaneevichitr, Chaowalit
    ;
    Kengkla, Nattarat
    ;
    Diewwanit, Onnjira
    The objective of this study was to improve the corrosion resistance of an A535 alloy by removing intermetallics on the alloy surface by alkaline etching to improve the morphologies and properties of the anodic film that was sealed with different sealants. It was found that alkaline etching for 4 min was suitable for dissolving intermetallic particles and simultaneously providing sufficient roughness for the adhesion of an oxide film to the Al matrix. The effect of alkaline etching revealed that a decrease in the intermetallic fraction from 21% to 16% after etching for 2 and 4 min, respectively, corresponded to the increase in the surface roughness, thickness, and consistency of the anodic film. It was also demonstrated that the surface morphology of the anodic films after stearic acid sealing was more uniform and compact than that after nickel fluoride sealing. The electrochemical polarization curves and salt spray test proved that the alloy etched for 4 min and sealed with stearic acid had better corrosion resistance as compared with the aluminum alloy sealed with nickel fluoride.