Physicochemical characterization of direct injection Engines's soot using TEM, EDS, X-ray diffraction and TGA
(2021-06-01)
Oo, Hay Mon
;
Karin, Preechar
;
Charoenphonphanich, Chinda
;
Chollacoop, Nuwong
;
Hanamura, Katsunori
The physical characteristics and elemental composition of particulate matters (PMs) from gasoline direct injection spark ignition (GDI-SI) engines were successfully investigated using transmission electron microscopy - energy dispersive X-ray spectroscopy (TEM-EDS). Thermogravimetric analysis (TGA) was used to analyze the PMs oxidation. The morphology of agglomerated GDI-PMs is not significantly different from the diesel direct injection compression ignition (DDI-CI) engine's PMs. The spherical single primary nanoparticles of the engine's soot composed of curve line carbon crystallites. The average diameter size of the single primary nanoparticles of GDI, DDI, and carbon black are approximately 24 nm, 26 nm, and 31 nm, while the inter-planar spacing is about 0.364 nm, 0.358 nm, and 0.356 nm, respectively. The total fringe lengths of GDI, DDI, and carbon black are approximately 154 nm, 159 nm, and 163 nm measured from the areas of 10 nm × 10 nm inner core regions of primary nanoparticles, and are 180 nm, 195 nm, and 228 nm from the outer shell regions, respectively. The total fringe lengths of inner core are shorter than the outer shell. Besides, the engine's PMs contains both crystalline and amorphous carbon structure using XRD analysis. The GDI-PMs had the least crystalline structure compared to the DDI-PMs and carbon black due to the higher percentage of amorphous fraction. TGA analysis showed that the GDI-PMs oxidation was faster than the DDI-PMs and CB-N330 oxidation because of the primary particle size, the fringe length, and the crystal size which have an impact on oxidation kinetics of particulate matters.
Some of the metrics are blocked by your
consent settings
Physicochemical characterization of forest and sugarcane leaf combustion's particulate matters using electron microscopy, EDS, XRD and TGA
(2021-01-01)
Oo, Hay Mon
;
Karin, Preechar
;
Chollacoop, Nuwong
;
Hanamura, Katsunori
Physical characteristics and quantitative elemental composition of PM and residual ash produced from sugarcane leaves (SCL) combustion were investigated using TEM-EDS compared with forest leaves (FRL). SEM-EDS was used to analyze the microstructure and chemical composition of biomass raw leaves and PM. XRD analysis was also performed to investigate the characterization of the crystalline nanostructure, structure of PM, and residual ash compared to the TEM image processing method. The oxidation kinetics of biomass raw materials, PM, and residual ash were investigated by TGA. The morphology of fine and ultrafine agglomerate structure of SCL soot and residual ash are not significantly different from the FRL soot and residual ash. The average diameter sizes of single primary nanoparticles of SCL and FRL soot are approximately 37 nm and 35 nm, while the sizes of residual ash are about 18 nm and 22 nm, respectively. The single primary nanoparticles of soot are mainly composed of curve line crystallites of carbon fringes, while residual ash is composed of straight-line lattice fringes. The average fringe lengths of SCL and FRL soot are about 1.25 nm and 1.04 nm from the outer shell and 0.89 nm and 0.74 nm from the inner core. The interlayer spacing of curve line carbon fringes of SCL and FRL soot is approximately 0.359 nm and 0.362 nm by the TEM image analysis and it was matched with XRD analysis. The biomass PMs are mainly composed of soot, Si, Ca, and K compounds: SiO<inf>2</inf>, CaCO<inf>3</inf>, and KCl.