    Enhancing the hydrogen permeation of alumina composite porous membranes via graphene oxide addition
    (2023-01-12)
    Hankoy, Montree
    ;
    Phrompet, Chaiwat
    ;
    Ruttanapun, Chesta
    ;
    Kaewpengkrow, Prangtip Rittichote
    ;
    Vichaphund, Supawan
    Graphene oxide (GO) membranes have attracted considerable interest for hydrogen (H<inf>2</inf>) purification applications. However, the addition of GO into matrix materials to enhance the efficiency of H<inf>2</inf> permeation remains a challenge. In this study, the fabrication of alumina/graphene oxide (AGO) composites containing varying contents of GO (0.5–3.0 wt.%) was investigated. The AGO composites were formed into pellets and sintered for 2 h at 1500 °C. Accordingly, the presence of GO in the membranes following sintering was confirmed by Raman spectroscopy. Additionally, the porosity of the AGO composites increased from 3.7% to 26.9% as the GO concentration increased from 0.5 wt.% to 3.0 wt.%. Furthermore, the average pore diameter of the AGO composites was in the range of 87–228 nm, and the pore size distribution was unimodal. The performance of the AGO membranes was investigated for the permeance of single gases H<inf>2</inf> and N<inf>2</inf> at 30–500 °C to evaluate their potential for H<inf>2</inf> separation applications. The AGO membranes with a GO addition of 2.5 and 3.0 wt.% exhibited a high hydrogen permeance of 232–410 × 10<sup>−6</sup> mol m<sup>−2</sup> s<sup>−1</sup> Pa<sup>−1</sup>, which was approximately 10 times greater than that of pristine Al<inf>2</inf>O<inf>3</inf> membrane. Additionally, the ideal H<inf>2</inf>/N<inf>2</inf> selectivity values ranged from 4.02 to 4.20. Furthermore, gas permeation through the AGO membrane was observed to follow the Knudsen diffusion mechanism.