Preparation of carbon aerogel microspheres by a simple-injection emulsification method
Author(s)
Date Issued
September 1, 2013
Type
Conference Paper
Abstract
Carbon aerogel microspheres were successfully prepared using a simple-injection emulsification method, employing sol-gel polycondensation of a resorcinol-formaldehyde solution containing sodium carbonate as a catalyst. This process was followed by solvent exchange using acetone, supercritical drying with carbon dioxide and carbonization in a nitrogen atmosphere. The effect of curing time before starting injection, injection rate and agitation rate of continuous phase on the particle size and the porous properties of the carbon aerogel microspheres was investigated. Adsorption of phenol by using the prepared carbon aerogel microspheres was also examined. The diameter of carbon aerogel microspheres was controlled in the range of 20-55 μm by varying injection rate and agitation rate. The mean diameter of carbon aerogel microspheres decreased with increasing the injection rate and the agitation rate, whereas their mean diameter was independent of the curing time. The BET surface area and total pore volume of carbon aerogel microspheres increased with increasing the curing time. In contrast, their BET surface area and total pore volume decreased with increasing the injection rate and the agitation rate. The BET surface area, total pore volume, mesopore volume and micropore volume of the carbon aerogel microspheres with a mean diameter of 45 μm were 903 m 2/g, 0.60 cm3/g, 0.31 cm3/g and 0.27 cm 3/g, respectively. The phenol-adsorption capacity of these carbon aerogel microspheres was 29.3 mg phenol/g adsorbent. © 2013 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.
Citation
Advanced Powder Technology, 24(5), 891-896, 2013