Effect of hydrated salts on the microstructure and phase transformation of poly(vinylidenefluoride-hexafluoropropylene) composites

Abstract

The present work has investigated a means of fabricating porous, β phase P(VDF-HFP) film by adding two kinds of hydrated metal salts. Without the use of mechanical stretching or electrical poling treatments, MgCl2 •6H2O and AlCl3 •6H2O are found to induce the formation of β phase crystals in porous film derived from the solution casting method. Trivalent Al ions have been found to effectively promote the self-oriented β phase of the P(VDF-HFP) film greater than divalent Mg ions. The overall β content is achieved about 38% and 42% for adding 0.25 wt% Mg- and Al-salts, respectively. The average pore sizes and surface roughness of porous P(VDF-HFP) films are increased with increasing salt concentration. The dielectric constant of about 5 for pure P(VDF-HFP) film (at 100 Hz) has been boosted up to 13-19 when adding the salts. In addition, the P(VDF-HFP) films filled with Al-salt exhibit the largest piezoelectric coefficient of 20 pC/N. Thus, the modified polymers are one of candidate materials for using in dielectric and piezoelectric applications.