Thermoelectric properties of Ni-doped CuAlO2
Author(s)
Wongcharoen, Ngamnit
Gaewdang, Thitinai
Date Issued
January 1, 2009
Type
Conference Paper
Abstract
The polycrystalline Ni-doped CuAlO2 were obtained by solid state reaction method. The mixture of high purity grade of CuO, Al2O 3 and Ni(NO3)2.6H2O powders was ground and then pressed by using uniaxial pressure. The obtained pellet was sintered in air at 1423 K for 24 h. XRD patterns showed the crystal structure of the as-sintered CuAl1-xNixO2 (0≤ x ≤0.10) belonging to rhombohedral, space group. No evidence of second phase was observed when Ni doping up to x = 0.01. At Ni content x ≥ 0.01 CuAl 1-xNixO2 solid solution phase along with the CuO and CuAl2O4 phases were observed. From SEM micrographs, the grain size decreased from 6 to 2 μm when the amount of Ni in CuAl1-xNixO2 samples increased. Hall mobility and hole concentration of the as-sintered samples were obtained from Hall effect measurements at room temperature. The activation energy values deduced from the electrical resistivity measurements as a function of temperature were reported. The variation of Seebeck coefficient and power factor as a function of temperature was also investigated. From the experimental results, the substitution of Ni2+ ion in Cu+ site of CuAl 1-xNixO2 material may be drawn. © 2009 Elsevier B.V. All rights reserved.
Citation
Physics Procedia, 2(1), 101-106, 2009