Electrical properties of nanostructure n-ZnSe/p-Si(100) heterojunction thin film diode
Author(s)
Wongcharoen, Ngamnit
Gaewdang, Thitinai
Date Issued
January 1, 2018
Type
Conference Paper
Abstract
The ZnSe/Si heterojunction is of specific interest since this structure provides effective solar cell and enables the integration of wide bandgap device in silicon circuits. It is known that the quality of the diode and the current transport mechanisms across the heterojunction may be greatly influenced by the quality of the interface and depends on the crystallinity of the film layer. In this work, n-ZnSe/p-Si(100) heterojunction was fabricated by thermal evaporating ZnSe thin films on p-Si (100) substrates. The current-voltage characteristics of n-ZnSe/p-Si(100) heterojunction were investigated in temperature range 20-300 K. Some important parameters such as barrier height, ideality factor and series resistance values evaluated by using thermionic emission (TE) theory and Cheung's method at room temperature are n = 2.910, øB0 = 0.832 eV and 8.59×103 Ω, respectively. The temperature dependence of the saturation current and ideality factor are well described by tunneling enhanced recombination at junction interface with activation energy and characteristic energy values about 1.293 eV and E00 = 95 meV, respectively. The carrier concentration of ZnSe thin films about 3.16×1013 cm-3 was deduced from the C-V measurements at room temperature. Admittance spectroscopy was employed for analysis of the defect energy levels situated in depletion region. The results showed that there was a single trap level whose position in the band gap was close to 0.04 eV above valence band. The results of this work may be useful for application such as heterojunction solar cells.
Citation
Key Engineering Materials, 775 KEM, 246-253, 2018