Facile Refluxing Synthesis of Hydroxyapatite Nanoparticles

Chaopanich, Pakvipar; Siriphannon, Punnama

doi:10.1071/CH14642

Facile Refluxing Synthesis of Hydroxyapatite Nanoparticles

Author(s)

Chaopanich, Pakvipar

Siriphannon, Punnama

Date Issued

January 1, 2015

Type

Article

DOI

10.1071/CH14642

Abstract

Hydroxyapatite (HAp) nanoparticles were successfully synthesized from an aqueous mixture of Ca(NO3)2·4H2O and (NH4)2HPO4 by a facile single-step refluxing method using polystyrene sulfonate (PSS) as a template. The effects of reaction times, pH, and PSS concentration on the HAp formation were investigated. It was found that the crystalline HAp was obtained under all conditions after refluxing the precursors for 3 and 6h. The longer refluxing time, the greater the crystallinity and the larger the crystallite size of the HAp nanoparticles. The HAp with poor crystallinity was obtained at pH 8.5; however, the well-crystallized HAp was obtained when reaction pH was increased to 9.5 and 10.5. In addition, the X-ray diffraction patterns revealed that the presence of PSS template caused the reduction of HAp crystallite size along the (002) plane from 52.6nm of non-template HAp to 43.4nm and 41.4nm of HAp with 0.05 and 0.2wt-% PSS template, respectively. Transmission electron microscopy images of the synthesized HAp revealed the rod-shaped crystals of all samples. The synthesized HAp nanoparticles were modified by l-aspartic acid (Asp) and l-arginine (Arg), having negative and positive charges, respectively. It was found that the zeta potential of HAp was significantly changed from +5.46 to -24.70mV after modification with Asp, whereas it was +4.72mV in the Arg-modified HAp. These results suggested that the negatively charged amino acid was preferentially adsorbed onto the synthesized HAp surface.

Citation

Australian Journal of Chemistry, 68(8), 1293-1298, 2015