Study on chemical structure stability and properties of chitosan-incorporated tamarind seed kernel xyloglucan hydrogels
Author(s)
Manamoongmongkol, Kanjana
Narkrugsa, Woatthichai
Phumjan, Lamphung
Permana, Lasuardi
Kaewbutra, Sasalux
Date Issued
December 5, 2024
Type
Article
Abstract
This study investigated the stability of chitosan-incorporated tamarind seed kernel xyloglucan hydrogels prepared at different ratios after storage for three years. The physical hydrogel samples were studied using ratios of xyloglucan to chitosan between 1.5:1 and 4:1, comparing fresh hydrogel with hydrogel stored for three years. The hydrogels were analyzed for Fourier transform infrared characteristics, rheological behavior, flow rate, and zeta potential. After three years of storage, a reversible reaction was confirmed by C-H molecular stretching using Fourier transform infrared. All hydrogel samples exhibited pseudoplastic fluid characteristics with liquid-like behavior. The zeta potential of fresh hydrogel at 1.5:1 and 4:1 ratios was 27.700 ± 0.964 mV and 22.633 ± 0.929 mV, respectively, whereas after three years, it became 28.067 ± 1.106 mV and 18.867 ± 0.503 mV, respectively. The amount of xyloglucan significantly affected the zeta potential of the xyloglucan-chitosan hydrogel, leading to a decrease in the stability of the hydrogel at a 4:1 ratio. The stability of the hydrogel at a ratio of 1.5:1 was confirmed by pH and zeta potential measurements. In conclusion, the properties and behavior of the xyloglucan-chitosan hydrogel remained stable after three years of storage at a 1.5:1 ratio.
Citation
Colloids and Surfaces A Physicochemical and Engineering Aspects, 702, 2024