Figures of merit of low-cost CuAl0.9Fe0.1O2 thermoelectric material prepared at different solid state reaction sintering temperatures
Author(s)
Date Issued
January 1, 2015
Type
Conference Paper
Abstract
In this study, we investigated a CuAl0.9Fe0.1O2 compound prepared at two different sintering temperatures in order to find out the effects of sintering temperature on the compound's figure of merit of thermoelectric properties. The thermoelectric CuAl0.9Fe0.1O2 compounds were prepared from high purity grade Cu2O, Al2O3 and Fe2O3 powders. The mixture of these powders were ground and then pressed with uniaxial pressure into pellets. The pellets obtained were sintered in the air at 1423K and 1473K. X-ray diffraction (XRD) patterns showed a single phase of CuAl0.9Fe0.1O2 with rhombohedral structure, R3¯m, along with a trace of CuO second phase. Moreover, the XRD peaks of the sample sintered at 1423K indicated that more Fe3+ atoms replaced Al3+ atoms in this sample than they did in the sample sintered at 1473K. The average grain size of the CuAl0.9Fe0.1O2 compound prepared increased with increasing sintering temperature, whereas its mean pore size and porosity decreased with increasing sintering temperature. The dispersed small pores markedly decreased the thermal conductivity of the compound, while the Fe3+ substitution of Al3+ increased its electrical conductivity. The highest figure of merit (ZT) found was 0.021 at 973K in the CuAl0.9Fe0.1O2 sample sintered at 1423K. Our findings show that this low-cost material with a reasonable figure of merit is a good candidate for thermoelectric applications at high-temperature.
Citation
Key Engineering Materials, 659, 185-189, 2015