Structural, morphological and adhesion properties of coFeB thin films deposited by DC magnetron sputtering
Author(s)
Ibuki, Chuleerat
Date Issued
October 29, 2013
Type
Conference Paper
Abstract
In this work the effects of amorphous (glass) and crystalline (Si) substrates on the structural, morphological and adhesion properties of CoFeB thin film deposited by DC Magnetron sputtering were investigated. It was found that the structure of a substrate affects to crystal formation, surface morphology and adhesion of CoFeB thin films. The X-Ray diffraction patterns reveal that as-deposited CoFeB thin film at low sputtering power was amorphous and would become crystal when the power increased. The increase in crystalline structure of CoFeB thin film is attributed to the crystalline substrate and the increase of kinetic energy of sputtering atoms. Atomic Force Microscopy images of CoFeB thin film clearly show that the roughness, grain size, and uniformity correlate to the sputtering power and the structure of substrate. The CoFeB thin film on glass substrate shows a smooth surface and a small grain size whereas the CoFeB thin film on Si substrate shows a rough surface and a slightly increases of grain size. Sticky Tape Test on CoFeB thin film deposited on glass substrate indicates the adhesion failure with a high sputtering power. The results suggest that the crystalline structure of substrate affects to the atomic bonding and the sputtering power affects to intrinsic stress of CoFeB thin film. © (2013) Trans Tech Publications, Switzerland.
Citation
Advanced Materials Research, 802, 47-52, 2013