The effects of foaming conditions on plasticized polyvinyl chloride foam morphology by using liquid carbon dioxide
Author(s)
Chuaponpat, N.
Date Issued
November 29, 2017
Type
Conference Paper
Abstract
This research studies the effects of foaming conditions by using liquid carbon dioxide (CO2) as a physical blowing agent on plasticized polyvinyl chloride (PVC) foam morphology. Foaming conditions were soaking time of 6, 10, and 12 h, foaming temperature of 70, 80, 90 °C for 5 s, at constant soaking temperature of -20 °C and pressure of 50 bar. Instantaneously increasing temperature was employed in this process for making foam structure. PVC foam samples were calculated percentage of shrinkage (Sh) by using density at before and after aging process at 30 °C for 12 h. When PVC samples were activated to form foam by using liquid CO2 as a physical blowing agent, it reveal bimodal foam structure with a thick bubble wall (10-20 μm). Bubble diameter of PVC foam at longer soaking time is in the range of 40-60 μm and its at shorter soaking time reveal a large bubble that is in the range of 80-120 μm. Foaming condition slightly affected to bubble density that was in the narrow range of 106-108 bubbles/cm3. PVC foam reveal reduction of density up to 65% when compare with PVC and Sh is less than 10%.
Citation
Iop Conference Series Materials Science and Engineering, 264(1), 2017