Structural, morphological, optical, and electrochemical properties of Zn-doped CeO2/rGO nanocomposites
Author(s)
Utara, Songkot
Salidkul, Nuchjaree
Karaphun, Attaphol
Chanlek, Narong
Hunpratub, Sitchai
Phokha, Sumalin
Date Issued
April 1, 2025
Type
Article
Abstract
Metal-doped cerium oxide has recently attracted the interest of researchers worldwide because of its various applications in different fields such as supercapacitors, high-sensitivity electrodes or photocatalytic. Metal-doped cerium oxide can be improved utilizing a variety of metals and composites with enhanced conductivity, which advances materials science in semiconductor processing. In this study, undoped and Zn-doped CeO2 nanoparticles at 5, 10, 15, and 20 at.% were reacted with reduced graphene oxide (rGO) using a hydrothermal method. They were heated at 150 °C for 12 h and then processed in an ultrasonic reactor (20 kHz) at 25 ± 1 °C. Their structural, morphological, elemental, optical, and electrochemical properties were systematically characterized. The calculated average crystallite sizes of CeO2 peaks ranged from 4.60 ± 0.2 to 12.0 ± 0.4 nm. These samples exhibited a single CeO2 phase corresponding to a face-centered cubic structure, except for 20 at.% Zn-doped CeO2/rGO, which presented a ZnO phase. The samples had lower band gap values than expected for undoped CeO2 nanoparticles, higher valence states due to their Ce3+/Ce4+ ratios, and a large surface area, 242 m2/g, due to Zn-doping in CeO2 samples. The highest specific capacitance values achieved were 88.49 F/g at 5 mV/s and 134.01 F/g at 0.5 A/g for undoped CeO2/rGO. Zn-doping resulted in decreased capacitive behavior with specific capacitance values in the range of 70.78–81.00 F/g at 5 mV/s and 79.24–101.43 F/g at 0.5 A/g. This study for synthesizing Zn/CeO2/rGO ternary nanocomposites produced materials with improved band gaps, valence states of Ce3+/Ce4+ ratios, and greater surface area for improved electrocatalytic performance.
Citation
Materials Science in Semiconductor Processing, 189, 2025