Beyond soft chemistry-bulk and surface modifications of polycrystalline lepidocrocite titanate induced by post-synthesis thermal treatment

Maluangnont, Tosapol; Chanlek, Narong; Suksawad, Thitiporn; Tonket, Nisarat; Saikhamdee, Panwarot; Sukkha, Usa; Vittayakorn, Naratip

doi:10.1039/c7dt03092d

Beyond soft chemistry-bulk and surface modifications of polycrystalline lepidocrocite titanate induced by post-synthesis thermal treatment

Author(s)

Maluangnont, Tosapol

Chanlek, Narong

Suksawad, Thitiporn

Tonket, Nisarat

Saikhamdee, Panwarot

Sukkha, Usa

Vittayakorn, Naratip

Date Issued

January 1, 2017

Type

Article

DOI

10.1039/c7dt03092d

Abstract

While the soft chemistry of layered alkali metal oxides is adequately understood, the effect of the post-synthesis thermal treatment on their structure, composition, and properties has been underexplored. In this article, we thoroughly investigated the bulk and surface modifications of K0.8M0.4Ti1.6O4 (M = Ni, Cu, Zn) lepidocrocite titanate thermally treated within 200 °C above its synthetic temperature under air. This practice was typically employed in e.g., specimen fabrication for physical property measurements. We observed the expansion of the interlayer distance (b/2) accompanied by a reduction in layer charge density. These findings can be explained by the deintercalation of interlayer K⁺ ions and the loss of intralayer Ti, M, and O species. Meanwhile, the enrichment of potassium and carbonate on the surfaces was evident. The slight differences in dielectric properties of the pellets thermally treated at different temperatures were attributed to the combination of bulk and surface modifications. At 10³ Hz and RT-250 °C, the maximum dielectric constants ϵ′max of ∼10⁴ with the dielectric loss (tan δ) ∼0.9-1.5 were obtained for K0.8Zn0.4Ti1.6O4.

Citation

Dalton Transactions, 46(41), 14277-14285, 2017