Fabrication of SWNTs/_-Fe2O3 as room-temperature LPG sensor

Abstract

A simple fabrication of liquid petroleum gas sensor based on SWNTs/α-Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> nanocomposite films is reported. SWNTs/α-Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films were successfully synthesized through the vertical floating catalyst chemical vapor deposition method using ferrocene-ethanol mist, followed by annealing in air at 350°C to create α-Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> . To fabricate a sensor, carbon conductive electrodes were directly deposited on top of the SWNTs/α-Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> films. SWNTs/α-Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> growth conditions (deposition time and ferrocene/ethanol ratio) were optimized to improve sensor response. The sensor had the capability to detect LPG at a concentration as low as 0.2% LEL (lower explosive limit), indicating possible applications in LPG monitoring at room temperature.