High-Temperature Deformation and Subsequent Static Recrystallization Behavior of Ultra-Low Stacking-Fault Energy Cu-Zn-Si Alloys

dc.contributor.authorMiura, Hiromi
dc.contributor.authorKasuya, Sanshiro
dc.contributor.authorOba, Yojiro
dc.contributor.authorOkada, Takuya
dc.contributor.authorWatanabe, Chihiro
dc.contributor.authorBenjanarasuth, Taworn
dc.date.accessioned2026-08-06T10:53:42Z
dc.date.available2026-08-06T10:53:42Z
dc.date.issued2026-01-01
dc.description.abstractBehaviors of high-temperature deformation followed by annealing and static recrystallization (SRX) in Cu-Zn-Si alloys with ultra-low stacking-fault energy (SFE) were investigated. The peak stress, steady-state flow stress and grain size during high-temperature deformation appeared to decrease with decreasing SFE, which would suggest easier occurrence of dynamic recrystallization (DRX) with decreasing SFE. Nevertheless, with increasing initial grain size, onset of DRX was much delayed even at higher temperatures and lower strain rates. SRX started after annealing for rather long periods of time contrary to the expectation that SRX should be stimulated because of meta-DRX. New grains evolved by DRX and SRX contained quite high density of annealing twins, showing DRX and SRX mechanisms induced by annealing twin formation during grain-boundary migration. [doi:10.2320/matertrans.MT-D2025015]
dc.identifier.citationMaterials Transactions, 67(6), 929-935, 2026
dc.identifier.doi10.2320/matertrans.MT-D2025015
dc.identifier.issn13459678
dc.identifier.other2-s2.0-105039819808
dc.identifier.urihttps://dspace.kmitl.ac.th/handle/123456789/17624
dc.sourceMaterials Transactions
dc.subjectCu-Zn-Si alloy
dc.subjectdynamic recrystallization
dc.subjecthigh-temperature deformation
dc.subjectmicrostructure
dc.subjectnucleation
dc.subjectstacking fault energy
dc.subjectstatic recrystallization
dc.titleHigh-Temperature Deformation and Subsequent Static Recrystallization Behavior of Ultra-Low Stacking-Fault Energy Cu-Zn-Si Alloys
dc.typeArticle

Files

Collections