    Item type:Publication,
    Valorization of horse manure conversion to magnetic carbon nanofiber for dye adsorption by hydrothermal treatment coupled with carbonization
    (2024-06-01)
    Kaewtrakulchai, Napat
    ;
    Chanpee, Sirayu
    ;
    Pasee, Warit
    ;
    Putta, Ampol
    ;
    Chutipaijit, Sutee
    Pollution of water resources has recently increased as a result of expanded industrial activity. Recycling waste biomass into bio-adsorbent material offers a cheap, easy, and eco-friendly solution. In this study, magnetic carbon nanofibers (MCNF) with a highly porous structure were developed from magnetite-preloaded horse manure by hydrothermal treatment followed by carbonization using different ratios of iron (III) nitrate and iron oxide as magnetic precursors. The produced MCNF had a very porous structure with specific surface area of 435.31 m<sup>2</sup>/g and high carbon content. The magnetic characteristics of MCNF promoted by the presence of iron oxide species. The saturated magnetization of MCNF obtained from a 5:5 ratio of the magnetic precursors (iron (III) nitrate: iron oxide) was 2.48 emu/g. Synthesized MCNF was applied as a bio-adsorbent for methylene blue (MB) removal from aqueous solution, with results showing excellent dye adsorption of 92–99 %. MB adsorption was facilitated by pore filling, electrostatic contact, hydrogen bonding, and ion complexation. Experimental results indicated that the Freundlich isotherm and pseudo-second-order kinetic models concurred with the observed MB adsorption data, suggesting that the adsorption mechanism involved multilayered micropore interactions between magnetite and MB chemisorption. The resulting magnetic adsorbent was successfully removed from the aqueous solution by physical separation. Findings indicated that horse manure-derived MCNF could be used as an efficient bio-adsorbent to remove organic contaminants in wastewater.
  • Loading...
    Thumbnail Image
    Some of the metrics are blocked by your 
    consent settings
    Item type:Publication,
    Magnetic Carbon Nanofibers from Horse Manure via Hydrothermal Carbonization for Methylene Blue Adsorption
    (2019-01-01)
    Kaewtrakulchai, Napat
    ;
    Putta, Ampol
    ;
    Pasee, Warit
    ;
    Fuangnawakij, Kajornsak
    ;
    Panomsuwan, Gasidit
    Disposal and recycle of waste biomass is of great concern. Thermochemically converting the waste biomass to carbon nanomaterials is an interesting because of environmental friendly, low cost and local availability. In this work, magnetic carbon nanofibers have been synthesized by hydrothermal and carbonization of the magnetite preloaded on horse manure which is controllable temperature and additive of catalyst. It was found that Fe is able to form magnetic carbon nanofibers (M-CNFs). Furthermore, magnetic carbon nanofibers were used as an adsorbent for methylene blue adsorption. Synthesized magnetic sorbents exhibited high performance on methylene blue adsorption and it is successfully separated from the water by magnetic separation.
  • Loading...
    Thumbnail Image
    Some of the metrics are blocked by your 
    consent settings
    Item type:Publication,
    Synthesis of carbon nanofiber from horse manure via hydrothermal carbonization for dye adsorption
    (2019-01-01)
    Pasee, Warit
    ;
    Puta, Ampol
    ;
    Sangnoi, Siwakron
    ;
    Wettayavong, Sorakit
    ;
    Kaewtrakulchai, Napat
    The livestock manure was suddenly concerned due to the crucial reason of greenhouse gases emission. Therefore, several technologies were applied to manage these waste materials such as fertilizer production, biogas or carbon material production. In this study, horse manure, a novel fibrous feedstock, was supplied to produce a carbon nanofiber for metal catalyst supporter and dye adsorbent. Carbon nanofiber was performed via hydrothermal carbonization at 200<sup>o</sup>C for 24 hours followed by carbonization at the temperature range of 300 to 900<sup>o</sup>C under the nitrogen atmosphere for 2 hours. Basically, the production yield, chemical compounds, surface morphology and pore size of produced carbon nanofiber were investigated. Dye adsorption capacity was increased by increase of carbonization temperature.