Preparation and characterization of hydroxyapatite/poly(ethylene adipate) hybrid composites
Date Issued
June 1, 2008
Type
Article
Abstract
Hydroxyapatite/poly(ethylene adipate) (HAp/PEA) composites were prepared by in situ ring-opening polymerization of cyclic oligo(ethylene adipate) (C-OEA) within the porous HAp templates. HAp was firstly prepared by a co-precipitation method using calcium hydroxide and phosphoric acid and then shaped as a rectangular porous template. PEA precursor was synthesized by bulk polymerization of dimethyl adipate and ethylene glycol in the presence of tetraisopropyl orthotitanate. C-OEA was obtained by cyclo-depolymerization of the PEA precursor under high dilution condition using dibutyl tinoxide as a catalyst. The HAp/PEA composites were prepared by immersing the porous HAp templates in the mixture solution of C-OEA and dibutyl tinoxide catalyst overnight and ring-opening polymerizing at 180, 200 and 220°C for 24 h. The ring-opening polymerized PEA formed as a thin film coating on the surface of porous HAp template. The HAp/PEA composites contained PEA in the range of 20-26 wt%. The weight-average molecular weights of ring-opening polymerized PEA were in the range of 3800-4450 g/mol. Compressive strength of the HAp/PEA composite was significantly increased from 25 MPa in the porous HAp template to 140 MPa in the composite. © 2008 VSP.
Citation
Journal of Biomaterials Science Polymer Edition, 19(7), 925-936, 2008