Luffa sponge offsets the negative effects of aeration on bacterial cellulose production
Author(s)
Date Issued
December 1, 2016
Type
Article
Abstract
Aims: To offset the negative effects of aeration on bacterial cellulose (BC) production by acetic acid bacteria using enmeshed cellulose microfibrils (CM) on luffa sponge matrices (LSM). Methods and Results: The CM were enmeshed on LSM (LSM-CM). The optimal amount of LSM-CM was determined for BC production under aerated conditions. Without LSM-CM, no BC was produced in seven out of nine production cycles at the highest aeration rate (9 l min−1). However, with 0·5% LSM-CM and an aeration rate of 3 l min−1, a satisfactory oxygen transfer coefficient was achieved, and also a good yield of BC (5·24 g l−1). Moreover, the LSM-CM was able to be recycled through nine consecutive BC production cycles. The highest BC yields (from 5·8 ± 0·4 to 6·6 ± 0·4 g l−1) were associated with high bacterial biomass and this was confirmed by scanning electron microscopy. Conclusions: We confirm that LSM-CM works well as a starter. Microenvironments low in dissolved oxygen within the matrices of LSM-CM are important for BC production under aeration conditions. Significance and Impact of the Study: The LSM-CM provides a microenvironment which offsets the negative effects of aeration on BC production. A sustainable, economic process for mass BC production is described using recycled LSM-CM with aeration.
Citation
Journal of Applied Microbiology, 121(6), 1665-1672, 2016