Effect of Pb (Yb 1/2Nb 1/2)O 3 on phase transition and thermal and electrical properties of PZ-PYbN solid solution on PZ-rich side

The (1 - x)PbZrO 3-xPb(Yb 1/2Nb 1/2)O 3 (PZ-PYbN) ceramics, with the compositions, x = 0.00-0.50, were prepared by the wolframite precursor method. The crystal structure and electrical and thermal properties of PbZrO 3 ceramic were investigated as a function of the composition, x, using X-ray diffraction, dielectric spectroscopy, hysteresis measurement and differential scanning calorimetry techniques. The results indicated that the solid solution, PZ-PYbN, changed from orthorhombic to rhombohedral symmetry when the amount of PYbN increased. The pyrochlore phase identified as Yb/Nb mixed compound was observed at the composition, x ≥ 0.2. For the compositions, x = 0.00-0.10, ceramics showed a sharp phase transition from AFE to PE. Furthermore, the intermediate FE phase was absent from the PZ-PYbN system. © 2011 Springer Science+Business Media, LLC.

Citation

Journal of Materials Science, 47(3), 1452-1459, 2012